872 Metre Oil Pipeline Restored with Composite Wrap


An underground oil pipeline at a Refinery in Spain was suffering from severe corrosion. If left unchecked, the pipeline, 872 metres (2860.8 ft) in length, would have incurred severe metal loss. As a result, disastrous consequences, both financially and also from an environmental perspective, could have ensued.

Figure 1. Corroded pipeline restored with composite wrap
Figure 1. Corroded pipeline restored with composite wrap

Solution Sought to Mitigate Cost and Carbon Footprint of Pipeline Replacement   

A prompt repair was required for the carbon steel pipeline, 55.9 cm (22 inches) in diameter, in order to mitigate any further corrosion damage being incurred. In fact, if left unrepaired, this would have caused the substrate to completely corrode through and, therefore, serious environmental issues could have ensued.  

A potential solution would have been to completely replace the pipeline. However, considering its mammoth length, this process would have required considerable financial expenditure and, furthermore, would incur a hefty carbon footprint.

For every ton of steel that is produced, 1.85 tons of CO₂ – nearly double the amount – is released back into the atmosphere (Carbon Clean). In addition to this, the process of removing and disposing of the damaged pipeline further ratchets up the carbon footprint of this process.

As well as the environmental impact of replacing the corroded pipeline, this process would also require a considerable period of downtime which would lead to further profit-loss. The combination of these factors, costly in both a financial and environmental sense, led the Customer to seek out an alternative solution to replacing the steel pipeline.  

Expensive Replacement Process Bypassed with Composite Wrap

The Customer decided to repair and protect the pipeline with a combination of polymeric technology in order to bypass the drawbacks associated with replacing the pipeline.

The following systems were specified and applied following an inspection from Elena Expósito Fernández, AMPP (NACE) Certified Coating Inspector Level 2 and Technical-Commercial Delegate at authorised Belzona Distributorship Rodator Composites:

Figure 2. Elena Expósito Fernández, Technical-Commercial Delegate at Rodator Composites

“The 2-part epoxy paste, Belzona 1111 (Super Metal), was specified to fill in any gaps in the weld seams to ensure the pipeline had a smooth profile. For heavily corroded areas, plate bonding was required using steel plates which were 50 cm x 60 cm (19.9 in x 23.6 in) in size, with a thickness of 5 mm (0.2 in). These were bonded into place using the epoxy structural adhesive, Belzona 7311. To reinforce the pipeline, the composite wrap, Belzona SuperWrap II, was specified. Finally, the anti-corrosion coating, Belzona 5811 (Immersion Grade), was chosen to provide long-term corrosion protection.

Elena Expósito Fernández

Technical-Commercial Delegate at authorised Belzona Distributorship Rodator Composites

Polymeric Technology Supports Decarbonisation of Oil and Gas Industry    

The Customer was able to successfully bypass the drawbacks associated with complete pipeline replacement by instead, opting to repair and protect the pipeline with a combination of polymeric technology. As well as making huge financial savings, this solution enabled the Customer to also minimise its environmental impact as well.

As the oil and gas industry continues to decarbonise, this latter point is particularly paramount. Polymeric technology is an extremely viable way in which oil and gas asset managers can make great strides in mitigating the carbon footprint of their facilities. An increased uptake in the use of cold-applied repair composites and protective coatings would help to accelerate the decarbonisation of this industry.

This article was originally published in International Oil & Gas Magazine.